Quote Originally Posted by everlastsupport View Post
An old saying, practice, practice, practice. It takes time. And A/O does not always make aluminum come easy on TIG.

I would bump up the post flow or at least stay over then end of the weld and let the gas shield it at the end of the weld (one you release the power). Looks like you are pulling away when the arc dies.

You will want many beads to get the feel and see how aluminum melts and flows, not quite as colorful and clear as steel.

Keep at it man.
Oops! That's what I've been doing ... as soon as I've let go of the trigger I've been pulling up my helmet to look at my weld ... my bad ... anxious to see what I've done so been jumping the gun,wow this is fun.